TY - JOUR AU - Ahmadi, Marziehsadat AU - Seyedjafari, Ehsan AU - Zargar, Seyed Jalal AU - Birhanu, Gebremariam AU - Zandi-Karimi, Ali AU - Beiki, Bahareh AU - Tuzlakoglu, Kadriye PY - 2017/05/23 Y2 - 2024/03/29 TI - Osteogenic differentiation of mesenchymal stem cells cultured on PLLA scaffold coated with Wharton's Jelly JF - EXCLI Journal JA - EXCLI J. VL - 16 IS - 0 SE - Original articles DO - 10.17179/excli2016-741 UR - https://www.excli.de/index.php/excli/article/view/434 SP - 785-794 AB - <p>Poly-L-lactic acid (PLLA) electrospun nanofiber scaffold is one of the most commonly used synthetic polymer scaffolds for bone tissue engineering application. However, PLLA is hydrophobic in nature, hence does not maintain proper cell adhesion and tissue formation, moreover, it cannot provide the osteo-inductive environment due to inappropriate surface characteristic and the lack of surface motives participating in the first cellular events. To modify these shortcomings different approaches have been used, among those the most commonly used one is coating of the surface of the electrospun nanofiber with natural materials. In this work Wharton's jelly (WJ), a tissue which surrounds the umbilical cord vessels, reaches in high amounts of extracellular matrix (ECM) components mainly; collagen, hyaluronic acid and several sulphated glycosaminoglycans (GAGs) were used to cover the surface of electrospun PLLA nanofiber scaffolds. The surface morphology of the nanofiber scaffold was evaluated via scanning electron microscope, and the <i>in vitro</i> osteogenic differentiation potential was determined by MTT assay and common osteogenic marker tests such as alkaline phosphatase (ALP) activity and calcium deposition tests. Coating of WJ could not change the surface morphology and diameter of the nanofibers. However, WJ-PLLA scaffolds showed higher proliferation of human mesenchymal stem cells (MSC) than tissue culture plate (TCP) and pristine PLLA scaffolds, moreover, WJ-PPLA scaffold demonstrated significant alkaline phosphatase activity and calcium mineralization than either TCP or PLLA nanofiber scaffolds.</p> ER -